DESCRIPTION
Main components and forming; High percentage chromium oxides and fused aluminum oxide, high temperature sintered with addition of special binders.
It is a series of patented products in China. The main components are combinations of aluminum chromium oxide solid solutions and spinels. Their excellent properties warrant their leading position in the industry: high bonding strength, high hardness, high refractoriness, good wearing resistance, good abrasion resistance, good thermal shock resistance and long service life.
APPLICATION
Suitable for synthetic ammonia gasification furnace and the bottom of steel heating furnace.
The products are widely used in various smelting vessels, including:
- Top blowing smelting furnaces: Ausmelt furnace, ISASMELT furnace, Kaldo furnace
- Side blowing smelting furnaces: Jinfeng furnace, Baiyin furnace, continuous converting furnaces, PS converters
- Bottom blowing smelting furnaces: SKS smelting furnace, QSL bottom-blowing furnace
- Submerged arc furnaces: Ti slag (TiO2 1 nickel-iron alloys, zinc alloy powders / metallic zinc (ZnO/Zn)
- Furnaces for treatment of environmental wastes: resource recovery from polluted environmental mud, waste electronics, anode slimes
- Other high temperature processing facilities: flash furnace, electric cleaning furnace for copper and nickel smelting, zinc volatilizing rotary kilns, electric zinc furnace, cement rotary kiln and glass kilns.
Scope of application: petroleum industry large and medium-sized synthetic ammonia furnace, steel furnace bottom, etc
The GW series products can provide service lives in multi-times to the conventional Cr-Mg, Mg-AI and aluminum silicate bricks
SPECIFICATION
| Model |
GWGJ-1 |
GWGJ-2 |
GWGJ-3 |
GWGJ-4 |
| Cold crushing Strength,Mpa ≥ |
100 |
90 |
80 |
100 |
| Bluk Density ,g/m³≥ |
3.1 |
3.0 |
3.0 |
3.8 |
| Apparent Porosity,%≤ |
17 |
17 |
18 |
13 |
| Fire ResistanceºC≥ |
1900 |
1800 |
1790 |
1850 |
| Reheat Linear Change(1500°Cx3h)% |
-0.2 |
-0.2 |
-0.3 |
+0.2 |
| Refractoriness under loadºC≥ |
1700 |
1700 |
1680 |
1700 |
| Thermal Expansion Coefficient(1300ºCx10^-6/ºC) |
8.6 |
8.3 |
7.6 |
6.8 |
| Thermal conductivity, (1200ºC)W/m.k≤ |
2 |
3 |
2 |
4 |
| 1250ºC Modulus of Rupture Mpa≥ |
9.5 |
8.7 |
9.1 |
8.9 |
CUSTOMIZED SHAPES
OUR ADVANTAGE
1. RICH EXPERIENCE
25 years'experience in the production of comprehensive refractories and many intellectual property rights.
2. ADVANCE EQUIPMENT AND STRONG TECHNICAL FORCE
Relying on scientific and technological innovation, the company has developed GW SA series spinel refractory products, and 10 new technologies have obtained national patents.
3. SPINEL REFRACTORIES FILL THE GAP IN DOMESTIC MARKET
The appearance of GW SA series spinel refractories developed and produced by our company has fundamentally solved the core problem of short life of furnace body caused by non-chemical corrosion resistance and non-liquid erosion resistance of supporting materials of user equipment.
ENGINGEERING CASES / SERVED PROJECTS
JINCHUAN GROUP CO., LTD.
MINSUR S.A. PERU, LIMA
PALABORA MINING COMPANY LTD (SOUTH AFRICA)
ANHUI KEWEI METAL MATERIALS CO., LTD
LIUZHOU HUAXI GROUP CO., LTD
KILN GROUP OF ZHUZHOU METALLURGICAL MACHINERY ENGINEERING
MINING PROJECT IN THE DRC
MILUMINSUR SMELTER
MENGZI MINING AND METALLURGY CO., LTD
SMELTER OF DAYE NONFERROUS METALS CO., LTD
GENE NICKEL CO., LTD
INDONESIA TIN COMPANY
BORA COPPER, INDIA
PERUVIAN ZINC COMPANY
MALAYSIA LEAD SMELTER
TECHNOLOGY CERTIFICATES
Audited Supplier 
){kind=link}